4,740 research outputs found
Charm Meson Mixing: An Experimental Review
We review current experimental results on charm mixing and CP violation. We
survey experimental techniques, including time-dependent, time-independent, and
quantum-correlated measurements. We review techniques that use a slow pion tag
from D*+ --> pi+ D0 + c.c. decays and those that do not, and cover two-body and
multi-body D0 decay modes. We provide a summary of D-mixing results to date and
comment on future experimental prospects at the LHC and other new or planned
facilities.Comment: 53 pages, 29 figures, 8 table
Structural behaviour of beam with HDPE plastic balls subjected to flexure load
This paper presents the structural behavior of reinforced concrete beam embedded with high density polyethylene balls (HDPE) subjected to flexural load. The HDPE balls with 180 mm diameter were embedded to create the spherical voids in the beam which lead to reduction in its self-weight. Two beam specimens with HDPE balls (RC-HDPE) and one solid beam (RC-S) with dimension 250 mm x 300 mm x 1100 mm were cast and tested until failure. The results are analysed in the context of its ultimate load, load-deflection profile, and crack pattern and failure mode. It was found that the ultimate load of RC-HDPE was reduced by 32% compared to RC-S beam while the maximum deflection at its mid span was increased by 4%. However, RC-HDPE is noticed to be more ductile compared to RC-S beam. Both types of beams experienced flexure cracks and diagonal tension cracks before failur
Improved Current Densities in MgB2 By Liquid-Assisted Sintering
Polycrystalline MgB2 samples with GaN additions were prepared by reaction of
Mg, B, and GaN powders. The presence of Ga leads to a low melting eutectic
phase which allowed liquid phase sintering and produces plate-like grains. For
low-level GaN additions (5% at. % or less), the critical transition
temperature, Tc, remained unchanged and in 1T magnetic field, the critical
current density, Jc was enhanced by a factor of 2 and 10, for temperatures of
\~5K and 20K, respectively. The values obtained are approaching those of hot
isostatically pressed samples.Comment: 12 pages, 1 table, 4 figures, accepted in Applied Physics Letter
- …